Epoxy Permabond
ET505
Description
A two-part epoxy adhesive curing at room temperature.
Operating temperatures
-40°C +80°C
Pre-packing
200ml400ml10kg40kg400kg
- Applications
- Advantages
- Features
Applications
It is suitable for bonding a wide variety of surfaces such as wood, metal, ceramics as well as many plastics and composite materials. It exhibits good resistance to exposure to gasoline, oils and water and has extended cure time what makes it the most suitable for large-scale production processes and for large batches output production.
Advantages
- Maximum gap fill is 1.5 – 2 mm
- Setting time is > 5 min
- High flexibility (operation under vibration and temperature drop conditions)
- Resistance to acids, alkolis and solvents
- Operable under steam conditions
- Operable in wet environment
- Resistace to technical natural gases
| Стандарт | Показатель | Ед. изм. | Значение |
|---|---|---|---|
| — | Цвет | Компонент А - бесцветный; Компонент В - янтарный | |
| — | Химический тип | Двухкомпонентная эпоксидная смола | |
| — | Диапазон рабочих температур | °С | от -40 до +80 |
| — | Динамическая вязкость | Па*с | Компонент А 23; Компонент В 17,5 |
| — | Плотность при 25 °С | г/см3 | Компонент А 1,2; Компонент В 1 |
| — | Относительное удлинение при разрыве | % | 10 |
| — | Твердость по Шору D | 73 | |
| ISO 4578 | Прочность на отрыв | Н/25 мм | 60 |
| ASTM D 1002 | Прочность на сдвиг для стали | МПа | 21 |
| — | Время для достижения рабочей прочности | ч | 380 |
| — | Время для достижения полной прочности | ч | 72 |
| — | Время для использования готовой смеси | мин | 120-150 |
| — | Максимально заполняемый зазор | мм | до 2 |
| — | Пропорции | 1 к 1 |